Room-Temperature Solid-State Lithium Metal Batteries Using Metal Organic Framework Composited Comb-Like Methoxy Poly(ethylene glycol) Acrylate Solid Polymer Electrolytes

Solid polymer electrolyte with good thermal stability and flexibility is an excellent candidate for solid-state lithium metal batteries, while its low ionic conductivity caused by high crystallinity limits its application at ambient temperature. Here a metal organic framework (zeolitic imidazolate framework-8, ZIF-8) composited comb-like methoxy poly(ethylene glycol) acrylate polymer electrolyte (MCPE) with high ionic conductivity (9.96 x 10(-5) S cm(-1) at 30 degrees C) is prepared by an in situ UV polymerization method. The as-prepared MCPE exhibits improved mechanical property due to the introduction of porous ZIF-8 nanofillers, which is beneficial to suppress the growth of lithium dendrites. Consequently, the LiFePO4||MCPE||Li cells show a high capacity of 116 mAh g(-1) at 30 degrees C and 0.5 C, and maintain 89.4% of initial capacity after 150 cycles with the average Coulombic efficiency of 99.9%. These results demonstrate that the MCPE shows great potential in solid-state lithium metal batteries near room temperature.