Nickel-iron layered silicate nanomembrane as efficient electrocatalyst for oxygen evolution reaction in alkaline media

Zhang，Jing1; Li，Zhaolong1; Bai，Guo1; Wang，Qingbing1; Zhang，Jin1; Wang，Wei2,3; Zhou，Liujiang4; Yi，Jiang5; Ma，Zhiyuan1

2023-01-15

10.1016/j.fuel.2022.126209

FUEL   影响因子和分区

0016-2361

Nickel-iron bimetal compounds have shown to be efficient electrocatalysts for the oxygen evolution reaction (OER) in alkaline environment. Here, we report the outstanding OER performance of an iron doped nickel layered silicate (NiFe)SiO(OH) (x = 0, 0.1, 0.2, 0.3 and 0.4), which was synthesized via a combined co-precipitation and hydrothermal method. The doping Fe ions are found to have a stronger adsorption effect on the *O intermediate, thereby reducing the energy barrier for the potential determining step *OH → *O, and as a result greatly enhance the OER activity of nickel layered silicate. At Fe doping concentration of 30 mol%, a minimum OER overpotential of 286 mV is achieved at the current density of 10 mA cm without IR correction, 86 mV lower than that of undoped catalyst. Moreover, the catalyst maintains favorable OER stability over a 24-hour chronopotentiometry test in 1 M KOH. This work provides insights into exploration and design of metal silicate-based OER catalysts.

DFT calculations Electrocatalytic water splitting Iron doping Layered silicate Oxygen evolution reaction

SCI ; EI

英语

其他

WOS:001006974500003

20224112863521

Design for testability ; Electrocatalysts ; Nickel compounds ; Potassium hydroxide ; Silicates

Chemical Agents and Basic Industrial Chemicals:803 ; Inorganic Compounds:804.2

ENGINEERING

2-s2.0-85139446874

Scopus

1.School of New Energy and Materials,Southwest Petroleum University,Chengdu,610500,China
2.School of Materials Science and Engineering,Beihang University,Beijing,100191,China
3.State Key Laboratory of Long-Life High Temperature Materials,Deyang,618000,China
4.School of Physics,University of Electronic Science and Technology of China,Chengdu,610054,China
5.Department of Mechanical and Energy Engineering,Southern University of Science and Technology,Shenzhen,518055,China

Zhang，Jing,Li，Zhaolong,Bai，Guo,et al. Nickel-iron layered silicate nanomembrane as efficient electrocatalyst for oxygen evolution reaction in alkaline media[J]. FUEL,2023,332.

Zhang，Jing.,Li，Zhaolong.,Bai，Guo.,Wang，Qingbing.,Zhang，Jin.,...&Ma，Zhiyuan.(2023).Nickel-iron layered silicate nanomembrane as efficient electrocatalyst for oxygen evolution reaction in alkaline media.FUEL,332.

Zhang，Jing,et al."Nickel-iron layered silicate nanomembrane as efficient electrocatalyst for oxygen evolution reaction in alkaline media".FUEL 332(2023).